Type: | Ep,Cc,Nn Belts |
---|---|
Material: | Rubber |
Inside Material: | Fabric |
Feature: | Oil-Resistant, Acid And Alkali Resistant, Tear-Resistant, Heat-Resistant, Cold-Resistant, Wear-Resistant |
Thickness: | 5-50mm |
Width: | 400-2600mm |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Item | 150ºC | 180ºC | 200ºC |
Tensile Strength | ≥14 N/mm2 | ≥14 N/mm2 | ≥13 N/mm2 |
Abrasion | ≤250 mm3 | ≤250 mm3 | ≤200 mm3 |
Elongation at break | ≥400% | ≥400% | ≥350% |
Const. Operating Temperature | ≤150 ºC |
≤180 ºC |
≤200 ºC |
Materials Carried | Lump Size | Temperature of Material Carried | Belt Surface Temperature |
Sintered Ore | 25-200 mm (1-8 inch) |
200-400ºC (390-750ºF) |
130-150ºC (270-300ºF) |
Return of Sintered Ore | Below 10 mm (0.4 inch) | 260ºC (480ºF) |
150-190ºC (300-370ºF) |
Coke | 100-200 mm (4-8 inch) |
70-100ºC (160-210ºF) |
50-60ºC (120-140ºF) |
Raw Material | Below 30 mm (1.2 inch) | 180-220ºC (360-410ºF) |
100-120ºC (210-250ºF) |
Clinker | 10-30 mm (0.4 - 1.2 inch) |
100-220ºC (210-440ºF) |
100-110ºC (210-230ºF) |
Cement | Powder | 100-125ºC (210-250ºF) |
80-90ºC (170-190ºF) |
Metal Powder | - | 170ºC (340ºF) |
120-130ºC (250-270ºF) |
Molding Sand | - | 200-250ºC (390-480ºF) |
80-90ºC (170-190ºF) |
Belt Type | Fabric Type | Single Fabric Strength (N/mm) | Single Fabric Thickness (mm) | Top+Bottom (mm) |
Ply | Width (mm) | Length (m/roll) |
|
Cotton Belt | CC--56 TC--70 |
56 70 |
1.10 1.0 |
2-8 1.5-8 |
0-4.5 0-4.5 |
2-12 | 300-2600 | 20-1000 |
Nylon Belt | NN100 | 100 | 0.70 | 2-10 | 300-2600 | 20-1000 | ||
NN150 | 150 | 0.75 | ||||||
NN200 | 200 | 0.90 | ||||||
NN250 | 250 | 1.15 | ||||||
NN300 | 300 | 1.25 | ||||||
NN400 | 400 | 1.50 | ||||||
EP Belt | EP100 | 100 | 0.75 | 2-8 | 300-2600 | 20-1000 | ||
EP150 | 150 | 0.85 | ||||||
EP200 | 200 | 1.00 | ||||||
EP250 | 250 | 1.20 | ||||||
EP300 | 300 | 1.35 | ||||||
EP350 | 350 | 1.50 | ||||||
EP400 | 400 | 1.65 |